Engineering Questions with Answers - Multiple Choice Questions
Polymer Engineering MCQ’s – Polypropylene
1 - Question
Which of the following kind of polymer has the highest percentage in polypropylene?
d) all of the mentioned
Explanation: The reaction conditions in the polymerization of propylene are varied so as to favour the formation of isotactic polymers. Commercial polypropylene is 90-97% isotactic.
2 - Question
What is the approximate density of the polypropylene?
a) 0.56 g/cm3
b) 0.90 g/cm3
c) 1.9 g/cm3
d) 0.68 g/cm3
Explanation: The density of polypropylene is about 0.90 g/cm3 and it also the lightest homo-polymer known.
3 - Question
What are the temperature and pressure conditions for the polymerization reaction of propylene?
a) 50-80 ᵒC and 5-25 atm
b) 50-80 ᵒC and 25-50 atm
c) 100-150 ᵒC and 5-25 atm
d) 100-150 ᵒC and 25-50 atm
Explanation: The polymerization reaction of propylene takes place at a temperature range of 50-80 ᵒC, generally at 60 ᵒC and at a low pressure range of 5-25 atm.
4 - Question
Which of the following is used as a catalyst in the polymerization of propylene?
Explanation: The polymerization of propylene take place by the Ziegler process in the presence of Ziegler Natta catalyst i.e. titanium halide and tri-alkyl aluminium.
5 - Question
Which of the solvent is used to check degree of isotacticity of polypropylene?
a) carbon tetra-cholirde
Explanation: The degree of isotacticity or isotactic index of polypropylene is calculated as the percentage of the polymer that is insoluble in n-heptane.
6 - Question
Which of the following properties of polypropylene makes it inferior, when compared with polyethylene?
b) tensile strength
d) stress cracking resitance
Explanation: Polypropylene becomes brittle when it is close to 0 ᵒC, and hence in this view it is inferior to polythelyene. Rest all other properties makes it superior to polyethylene as it has high tensile strength and clarity, and is occupied with less stress cracking problems.
7 - Question
Which among the following polymers is more prone to oxidation or aging?
d) None of the mentioned
Explanation: Polypropylene is more prone to oxidation and aging than LDPE and HDPE, as it contains higher concentration of tertiary carbons.
8 - Question
Which of the following is not a reaction variable for polymerization of polypropylene?
a) molar ratio of catalyst composition
b) catalyst concentration
c) reaction temperature
d) none of the mentioned
Explanation: All the three variables, molar ratio of catalyst composition, catalyst concentration, and the reaction temperature are the reaction variable for the polymerization reaction of polypropylene.
9 - Question
Where among the following fields polypropylene cannot be used?
a) insulating cables and wires
b) home appliances
c) automobile appliances
Explanation: Polypropylene is used in the form of typical mouldings, which include components like automobile and home appliances, furniture and kitchenware, etc. and is not used for insulation purposes.